| Chinese | English |
| 中间包内取样位置 | sampling position in tundish |
| 包样分析 | ladle sample analysis |
| 包样切割器 | ladle sample cutter |
| 包样制备 | ladle sample preparation |
| 包样平均值 | average ladle sample value |
| 包样形状 | ladle sample shape |
| 包样形状 | ladle sample geometry |
| 包样成分 | ladle sample composition |
| 包样成分 | ladle chemistry |
| 包样抛光机 | polishing machine for ladle sample |
| 包样断面 | ladle sample section |
| 包样标准偏差 | ladle sample standard deviation |
| 包样算术平均值 | arithmetic average value of ladle sample |
| 包样缩分 | ladle sample reduction |
| 包样试验 | ladle test |
| 包样试验 | ladle sample test |
| 包样重量 | ladle sample weight |
| 试样包埋 | specimen embedding |
| 钢包试样 | ladle sample (A substantial decrease (> 0.005 percent) in the soluble aluminium content between the last ladle sample and mold is an excellent indication of a reoxidation problem at the caster. 结晶器(钢水中)溶解铝含量如果比钢包最后一次试样溶解铝含量大幅度降低(>0.005%),那么这是连铸机存在二次氧化问题的最好标志。) |
| 铸包取样 | pit sample |